Corrosion inhibitor compositions comprising tetrahydrobenzotriazoles and other triazoles and methods for using same

ABSTRACT

A composition with a corrosion inhibitor component having one or more tetrahydrobenzotriazoles and one or more other triazoles; wherein the tetrahydrobenzotriazoles are in a weight ratio to the other triazoles such that the composition decreases the General Corrosion rate, as measured by copper electrodes in the presence of 10 ppm sodium hypochlorite, by at least about 0.05 mpy relative to a corrosion inhibitor component which is 100% of the other triazoles. Also, a method of using this composition to inhibit corrosion of a metal component which has a metal or metal alloy which is corrodible in the presence of copper or copper corroding agents.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional of U.S. application Ser. No. 13/045,638 filed Mar. 11, 2011. The entire disclosure and contents of the above referenced application is hereby incorporated by reference.

FIELD OF THE INVENTION

The present invention generally relates to a corrosion inhibiting composition comprising one or more tetrahydrobenzotriazoles and one or more other triazoles. The present invention also generally relates to a method for inhibiting corrosion of a metal component which is corrodible in the presence of copper or copper corroding agents by contacting that metal component with a corrosion inhibiting amount of this composition.

BACKGROUND

In many industrial processes, undesirable excess heat may be removed by the use of heat exchangers in which aqueous systems may be used as the heat exchange fluid. Various metals and metal alloys, such as copper and copper-bearing alloys (e.g., brass), may be used in the fabrication of such heat exchangers, as well as in other parts in contact with the cooling water, such as pump impellers, stators, valve parts, etc. Aqueous systems such as those cooling fluids may be corrosive towards these copper-containing metal parts due to the presence of aggressive ions and by the intentional introduction of oxidizing substances for biological control. The consequences of such corrosion are the loss of metal from the equipment, potentially leading to failure or requiring expensive maintenance, creation of insoluble corrosion product films on the heat exchange surfaces, potentially leading to decreased heat transfer and subsequent loss of productivity, and discharge of copper ions which may then “plate out” on less noble metal surfaces and may cause severe galvanic corrosion, a particularly insidious form of corrosion. Also, copper is a potentially toxic substance, so its discharge to the environment is undesirable.

It is common practice to introduce corrosion inhibitors into such cooling water systems, as well as other aqueous and nonaqueous systems. These corrosion inhibitors may interact with the metal/metal alloy to directly produce a film which is resistant to corrosion, or may indirectly promote formation of protective films by activating the metal/metal alloy surface so as to form stable oxides, other insoluble salts, etc. Such protective films may not be completely stable, but may instead degrade under the influence of the aggressive conditions in the cooling water. Because of this degradation, a constant supply of corrosion inhibiting substances in the cooling water may be required to inhibit corrosion of the metal/metal alloy surface.

In general, the corrosion inhibiting performance of these corrosion inhibitors in industrial water systems (as well as in other systems, for example, other heat transfer systems, lubricant systems, hydraulic fluid systems, etc.) may be judged by their passivation and persistency characteristics. Improved film persistence is recognized as one of the criteria for film-forming corrosion inhibitors in view of the economic and ecologic advantages of the commensurate low dose or charge required for corrosion inhibiting compositions that may attain such persistence. Passivation rate is also a relevant criterion for the same reasons. In other words, those compositions that provide the most valuable corrosion inhibiting films are those which both form quickly, thus minimizing the presence of the corrosion inhibiting composition in the effluent, as well as persist for greatest length of time, likewise minimizing the need to continually charge the corrosion inhibiting composition into the system.

SUMMARY

According to a first broad aspect of the present invention, there is provided a composition comprising a corrosion inhibiting component having:

-   -   one or more tetrahydrobenzotriazoles having the general formulas         Ia or Ib:

-   -   wherein R₁ is one or more of: H, a hydroxy group, or an         aliphatic group; and wherein R₂ is H, or an aliphatic group; or         salts of the tetrahydrobenzotriazoles; and     -   one or more other triazoles having the general formula II:

-   -   wherein R₃ is one or more of H, a hydroxy group, an aliphatic         group, or an aromatic group; and wherein R₄ is H, or an         aliphatic group; or salts of the other triazoles;     -   wherein the tetrahydrobenzotriazoles are in a weight ratio to         the other triazoles such that the composition decreases the         General Corrosion rate, as measured by copper electrodes in the         presence of 10 ppm sodium hypochlorite, by at least about 0.05         mpy relative to a corrosion inhibitor component comprising 100%         of the other triazoles.

According to a second broad aspect of the present invention, there is provided a method comprising the following steps:

-   -   (a) providing a composition comprising a corrosion inhibiting         component having:         -   one or more tetrahydrobenzotriazoles having the general             formulas Ia or Ib:

-   -   -   wherein R₁ is one or more of: H, a hydroxy group, or an             aliphatic group; and wherein R₂ is H, or an aliphatic group;             or salts of the tetrahydrobenzotriazoles; and         -   one or more other triazoles having the general formula II:

-   -   -   wherein R₃ is one or more of H, a hydroxy group, an             aliphatic group, or an aromatic group, R₄ is H, or an             aliphatic group; or salts of the other triazoles;         -   wherein the tetrahydrobenzotriazoles are in a weight ratio             to the other triazoles such that the composition decreases             the General Corrosion rate, as measured by copper electrodes             in the presence of 10 ppm sodium hypochlorite, by at least             about 0.05 mpy relative to a corrosion inhibitor component             comprising 100% of the other triazoles; and

    -   (b) contacting a metal component which comprises a metal or         metal alloy which is corrodible in the presence of copper or         copper corroding agents with a corrosion inhibiting amount of         the composition of step (a) to inhibit corrosion of the metal         component by copper or copper corroding agents.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention will be described in conjunction with the accompanying drawing, in which:

The FIGURE represents a graphical plot of individual data points which compare the General Corrosion rates (at 25° C.), as measured by copper (Cu) electrodes, reflected in units of milli-inches per year (mpy), in the presence of two sequentially added aliquots of 5 ppm sodium hypochlorite (total of 10 ppm of sodium hypochlorite added), wherein the Cu electrodes are “passivated” with (i.e., coated with a film of) compositions comprising 90% by weight of various triazole blends and 10% by weight propylene glycol.

DETAILED DESCRIPTION

It is advantageous to define several terms before describing the invention. It should be appreciated that the following definitions are used throughout this application.

Definitions

Where the definition of terms departs from the commonly used meaning of the term, applicant intends to utilize the definitions provided below, unless specifically indicated.

For the purposes of the present invention, the term “comprising” means various compositions, compounds, ingredients, components, elements, capabilities and/or steps, etc., may be conjointly employed in the present invention. Accordingly, the term “comprising” encompasses the more restrictive terms “consisting essentially of” and “consisting of.”

For the purposes of the present invention, the term “tetrahydrobenzotriazoles” (referred to interchangeably herein as “tetrahydrogenated benzotriazoles” or “THBs”) refers to one or more compounds having the general formulas Ia or Ib:

wherein R₁ is one or more of H, a hydroxy group, or an aliphatic group: and wherein R₂ is H, or an aliphatic group; as well as salts of these compounds of formulas Ia or Ib. The aliphatic R₁ groups may be at one or more of the 4, 5, 6 and/or 7 positions on the cyclohexane ring. In the some embodiments, R₁ may be one aliphatic group, with the remaining R₁ being H. The salts of these tetrahydrobenzotriazoles may include, for example, the sodium salts, the potassium salts, the ammonium salts, etc. These tetrahydrobenzotriazoles may include, for example, tetrahydrobenzotriazole (i.e., 4,5,6,7-tetrahydro-benzotriazole, also referred herein interchangeably as “THBT”), tetrahydrotolyltriazole (referred to herein interchangeably as tetrahydrotoluyltriazole or “THBT”) which may be 4-methyl-1H-benzotriazole, 5-methyl-1H-benzotriazole, or a mixture thereof; sodium, potassium, or ammonium salts of THBT or THTT; etc., as well as blends, mixtures, etc., of these tetrahydrobenzotriazoles. See, for example, U.S. Pat. No. 3,597,353 (Randell et al.), issued Aug. 3, 1971; and U.S. Pat. No. 3,849,433 (Butula et al), issued Nov. 19, 1974, the entire contents and disclosures of which are herein incorporated by reference, for how to prepare tetrahydrobenzotriazoles from the respective benzotriazoles by catalytic hydrogenation, and which may also provide residual unhydrogenated benzotriazoles as the other triazoles for embodiments of compositions of the present invention.

For the purposes of the present invention, the term “other triazoles” refers to one or more compounds having the general formula II:

wherein R₃ is one or more of: H, a hydroxy group, an aliphatic group, or an aromatic group, R₄ is H, or an aliphatic group; as well as salts of these compounds of formula II (e.g., sodium salts, potassium salts, ammonium salts, etc.). The one or more R₃ groups may be at one or more of the 4, 5, 6 and/or 7 positions on the benzene ring. In the some embodiments, R₃ may be one aliphatic group, with the remaining R₃ being H. These other triazoles may include benzotriazole (referred to herein interchangeably as “BT”), tolyltriazole (referred to herein interchangeably as toluyltriazole or “TT”) which may be 4-methyl-benzotriazole (referred to herein interchangeably as “4-MeBT”); 5-methyl-benzotriazole (referred to herein interchangeably as “5-MeBT”), or a mixture thereof; butyl-benzotriazole (referred to herein interchangeably as “BBT”) which may be, for example, 4-butyl-benzotriazole, 5-butyl-benzotriazole, or a mixture thereof; pentoxy-benzotriazole (referred to herein interchangeably as “Pentoxy BT”) which may be 4-pentoxy-benzotriazole (referred to herein interchangeably as “4-Pentoxy BT”), 5-pentoxy-benzotriazole (referred to herein interchangeably as “5-Pentoxy BT”), or a mixture thereof carboxy-benzotriazole (referred to herein interchangeably as “Carboxy BT”) which may be 4-carboxy-benzotriazole (referred to herein interchangeably as “4-Carboxy BT”), 5-carboxy-benzotriazole (referred to herein interchangeably as “5-Carboxy BT”), or a mixture thereof as either the acid(s) or a water-soluble salt(s) thereof (e.g., sodium salt, potassium salt, etc.); N-1-bis(2-ethylhexyl)-aminomethyl-tolyltriazole (e.g., sold by Ciba Specialty Chemicals under the trade name Irgamet 39®); N-1-bis(2,2′-ethanol)-aminomethyl-tolyltriazole (e.g., sold by Ciba Specialty Chemicals under the trade name Irgamet 42®); sodium, potassium, or ammonium salts of, for example, TT, BT, or BBT; etc.

For the purposes of the present invention, the term “aliphatic” refers to a carbon-containing moiety other than an aromatic moiety. Aliphatic moieties may be straight chain, branched chain, cyclic (cycloaliphatic), or any combination thereof, may be substituted or unsubstituted, may include one or more heteroatoms (e.g., oxygen atoms, nitrogen atoms, sulfur atoms, etc.) in the carbon chain (i.e., may be heterocyclic), may be unsaturated (i.e., one, two or more double bonds) or saturated, etc, and may have any desired number of carbon atoms, e.g., from 1 to 30 carbon atoms, for example from 1 to 12 carbon atoms, such as from 1 to 7 carbon atoms, (e.g., from 1 to 4 carbon atoms), etc. Aliphatic moieties suitable herein may include, but are not limited to, substituted or unsubstituted alkyl, alkenyl, alkadienyl, alkynyl, cycloalkyl, cycloalkenyl, etc. Suitable aliphatic moieties may include, but are not limited to, straight or branched chain alkyl (e.g., methyl, ethyl, propyl, isopropyl, butyl, isobutyl, pentyl, hexyl, heptyl, etc.) and substituted alkyl (e.g., hydroxylmethyl, hydroxyethyl, trifluoromethyl, alkoxymethyl, etc.), alkoxy, substituted amino (e.g., dimethylamino, etc.), carboxy, ester, amide, sulfonamide, carbamate, acyl (i.e., aldehyde or keto), etc., or any combination thereof.

For the purposes of the present invention, the term “aromatic” refers to an unsaturated cyclic arene moiety containing one or more unsaturated cyclic rings (for example, 5 and/or 6 atoms per ring) that may be substituted, unsubstituted, or a combination thereof, may be heterocyclic (i.e., including one or more oxygen atoms, nitrogen atoms, sulfur atoms, etc.), nonheterocyclic, or a combination thereof, may have any desired number of carbon atoms, e.g., from 3 to 30 carbon atoms, for example, from 3 to 18 carbon atoms, e.g., from 3 to 12 carbon atoms, etc. Aromatic moieties suitable herein may include, but are not limited to, substituted or unsubstituted phenyl, naphthyl, biphenyl, binaphthyl, phenanthenryl, anthracenyl, pyridinyl, pyrimidinyl, purinyl, pyrinyl, furanyl, thiophenyl, benzofuranyl, benzothiophenyl, dibenzofuranyl, dibenzothiophenyl, imidazolyl, oxazolyl, thiazolyl, pyrazolinyl, indolyl, pyridazinyl, pyrazinyl, quinolinyl, isoquinolinyl, benzoquinolinyl, phenanthrolinyl (e.g., 1,10-phenanthrolyl), carbazolyl, etc. Suitable aromatic moieties may include, but are not limited to, aromatics substituted with straight or branched chain alkyl (e.g., methyl, ethyl, propyl, isopropyl, butyl, isobutyl, pentyl, hexyl, heptyl, etc.) and substituted alkyl (e.g., hydroxymethyl, hydroxyethyl, trifluoromethyl, alkoxymethyl, etc.), amino and substituted amino (e.g., dimethylamino, etc.), hydroxy (e.g., a phenolic), carboxy, sulfonate, ester, amide, sulfonamide, carbamate, acyl (i.e., aldehyde or ketone), nitro, etc., or any combination thereof.

For the purposes of the present invention, the term “tetrahydrobenzotriazole activating solvents” refers to those solvents which enhance, improve, reduce the variability of, etc., the corrosion inhibiting ability, effectiveness, etc., of tetrahydrobenzotriazoles. These tetrahydrobenzotriazole activating solvents are generally polar and are capable of solubilizing the tetrahydrobenzotriazoles, as well as other triazoles. These tetrahydrobenzotriazole activating solvents may include one or more of the following: aliphatic alcohols having, for example, from 1 to 6 carbon atoms, such as methanol, ethanol, propanol, isopropanol, butanol, isobutanol, pentanol, isopentanol, hexanol, isohexanol, etc.; low-molecular weight hydroxyl-containing polyol compounds, such as propylene glycol (1,2-propylene glycol and/or 1,3-propylene glycol), ethylene diglycol, diethylene glycol, triethylene glycol, dipropylene glycol, butylene glycol, butyl diethylene glycol, glycerol, etc.; monoethers of glycols such as methyl, ethyl, propyl and/or butyl monoethers of ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, etc.; higher molecular weight nonionic alkylene oxide polyol adduct(s) having a molecular weight of more than about 400, such as, for example, polyethylene glycol, polypropylene glycol, random-added polypropylene polyethylene glycols, or block copolymers of ethylene and propylene oxide sometimes referred to as poloxamers (e.g., Pluronics®); etc.

For the purposes of the present invention, the term “metal component” refers to any part, piece, tool, machine, etc., which comprises one or more metals or metal alloys. Metal components may include heat exchangers, pumps, pump impellers, stators, valve parts, evaporators, boilers, metal working tools, containers, drums, barrels, pipe, ducts, drums, cylinders, conduits, plumbing, etc.

For the purposes of the present invention, the term “metal or metal alloy which is corrodible in the presence of copper or copper corroding agents” refers to a metal or metal alloy which, when in contact with, exposed to, etc., copper (e.g., copper ions) or a copper corroding agent, may lose at least a portion of the metal or metal alloy due to a chemical or an electrochemical corrosive process. In the case of metals or metal alloys which include one or more of aluminum, steel, iron, (e.g., cast iron), silver, etc., which may corrode in the presence of copper, the corrosive process is primarily electrochemical where, for example, copper ions “plate out” from an electrolytic solution onto the metal or metal alloy and thus cause “galvanic corrosion.” In the case of metals or metal alloys such as copper, brass, bronze, etc., which corrode in the presence of a copper corroding agent (e.g., hypochlorite), the corrosive process is primarily chemical where, for example, copper is dissolved from the surface of the metal component, and forms copper ions in the fluid in contact with the metal component surface.

For the purposes of the present invention, the term “galvanic corrosion” refers conventionally to an electrochemical process in which one metal corrodes preferentially when in electrical contact with a different type of metal, and wherein both metals are immersed in, in contact with, in the presence of, etc., an electrolyte-containing fluid.

For the purposes of the present invention, the term “corrosion inhibitor” refers to a material, substance, composition, compound, component, etc., which reduces, decreases, diminishes, lowers, minimizes, etc., the rate of corrosion (e.g., General Corrosion rate) of a metal or metal alloy from the surface of a metal component in the presence of copper or a copper corroding agent.

For the purposes of the present invention, the term “corrosion inhibiting amount” refers to an amount of a material, substance, composition, compound, component, etc., which is effective to provide a measurable degree of reduction, diminution, drop, decrease, etc., in the rate of corrosion (e.g., General Corrosion) of metal or metal alloy from the surface of a metal component in the presence of copper or a copper corroding agent.

For the purposes of the present invention, the term “aqueous system” refers to any system containing metals which contain or are in contact with aqueous fluids on a regular basis. Aqueous systems may include open recirculating cooling systems which obtain their source of cooling by evaporation, closed loop cooling systems, boilers and similar steam generating systems, heat exchange equipment, reverse osmosis equipment, oil production systems, flash evaporators, desalinization plants, gas scrubbers, blast furnaces, paper and pulp processing equipment, steam power plants, geothermal systems, food and beverage processing equipment, sugar evaporators, mining circuits, bottle washing equipment, soil irrigation systems, closed circuit heating systems for residential and commercial use, aqueous-based refrigeration systems, down-well systems, aqueous machining fluids (e.g., for use in boring, milling, reaming, broaching, drawing, turning, cutting, sewing, grinding and in thread-cutting operations, or in non-cutting shaping, spinning, drawing, or rolling operations), aqueous scouring systems, aqueous glycol anti-freeze systems, water/glycol hydraulic fluids, ferrous-surface pre-treatment, polymer coating systems, etc. These aqueous systems may include various sources of water, for example, fresh water, brackish water, sea water, brines, sewage effluents, industrial waste waters, etc.

For the purposes of the present invention, the term “oxidants” refers to materials, substances, compositions, compounds, etc., which are present in or added to, for example, aqueous systems to oxidize other components present in these systems, for example, are used as biocides for aqueous systems. These oxidants may include, for example, chlorine-containing oxidants, such as, for example, chlorine, chlorine dioxide, sodium chlorite, hypochlorous acid, hypochlorites (e.g., sodium hypochlorite, calcium hypochlorite, etc.), chlorine bleach, etc., nonchlorine-containing oxidants such as acids (e.g., sulfuric acid, nitric acid, etc.), caustics (e.g., sodium hydroxide, potassium hydroxide, etc.), nonchlorine bleach, peroxides (e.g., hydrogen peroxide, sodium peroxide, etc.), ozone, etc.

For the purposes of the present invention, the term “copper corroding agent” refers to materials, substances, compositions, compounds, etc., which causes, increases, etc., loss of copper (including copper present in copper alloys such as brass, bronze, etc.) from the surface of metal components. These copper corroding agents may include, for example, chlorine-containing oxidants such as chlorine, chlorine dioxide, sodium chlorite, hypochlorous acid, hypochlorites, (e.g., sodium hypochlorite, calcium hypochlorite, etc.), chlorine bleach, etc., as well s nonchlorine-containing oxidants such acids (e.g., sulfuric acid, nitric acid, etc.), caustics (e.g., sodium hydroxide, potassium hydroxide, etc.), nonchlorine bleach, peroxides (e.g., hydrogen peroxide, sodium peroxide, etc.), ozone, etc.

For the purposes of the present invention, the term “organic fluid” refers to those fluids (other than tetrahydrobenzotriazoles, other triazoles, and tetrahydrobenzotriazole activating solvents) which comprise at least carbon and hydrogen, (e.g., hydrocarbon), but which may comprise other atoms such as oxygen, nitrogen, halogen, etc. These organic fluids may include, for example, one or more of petroleum, petroleum derivatives and petroleum distillates (e.g., mineral oil, lubricating oils, etc.); animal fats: plant oils; synthetic oils (e.g., polyol esters, alkylated naphthalenes, alkylated benzenes, etc.); hydroprocessed oils; etc., which may function as lubricants, coolants, metal working fluids, anti-wear fluids, anti-friction fluids, etc.

For the purposes of the present invention, the term “metal working fluid” refers to any fluid which is liquid and which may be used in a metal working process for one or more functions, which may include cooling, lubrication, debris removal, reducing or inhibiting corrosion, reducing or inhibiting material build up on workpieces and/or metal working tools, etc. Metal working fluids may also be referred to interchangeably as a “cuffing fluid,” a “cutting oil,” a “cutting compound,” etc. The metal working fluid may be aqueous, may be an oil-in-water emulsion, may be a paste, may be a gel, may be a mist, etc. These metal working fluids may include water for example, in amounts of from 5 to about 70% by weight, such as from about 15 to about 50% by weight of the metal working fluid), conventional coolants and lubricants such as, for example, one or more of: a monocarboxylic acid(s), which may have more than 10 carbon atoms, such as fatty acids having from 12 to 18 carbon atoms; an aromatic or paraffinic carboxylic acid, such as, for example, an alkylsulfuramido carboxylic acid, an arylsulfuramido carboxylic acid, alkenyl dicarboxylic acid, and/or a alkylphenyl carboxylic acid disclosed in, for example, U.S. Pat. No. 4,315,889 (McChesney et al.), issued Feb. 16, 1982, the entire disclosure and contents of which is hereby incorporated by reference; a petroleum distillate(s) (e.g., mineral oil), an animal fat(s), a plant oil(s), etc. The amount of the lubricant/coolant may comprise, for example, from about 1 to about 30% by weight of the metal working fluid.

For the purposes of the present invention, the term “metal working tool” refers to any tool which causes primarily physical changes, as opposed to chemical changes, to a workpiece. Metal working tools may include, for example, drills, drill presses, mills, cutters, planers, lathes, shapers, borers, reamers, grinders, stamping press, scrapers, etc.

For the purposes of the present invention, the term “metal working process” refers to any mechanical process which uses a metal working tool. Such processes may include, for example, drilling, milling, cutting, planing, machining, shaping, stamping, grinding, lathing, trimming, abrading, boring, reaming, polishing, turning, honing, sawing, broaching, tapping, threading etc., or any combination thereof.

For the purposes of the present invention, the term “passivation” refers to the formation of a film which lowers the corrosion rate (e.g., General Corrosion rate) of the metallic surface being treated, usually by continuously or intermittently charging a dose of the film forming material directly into the water of the system to be treated.

For the purposes of the present invention, the term “passivation rate” refers to the time required to form a protective film on a metallic surface.

For the purposes of the present invention, the term “persistency” refers to the length of time a protective film is present on a metal/metal alloy surface when a corrosion inhibitor is not present in the fluid system (e.g., an aqueous system) which is in contact with the protected metal/metal alloy surface.

For the purposes of the present invention, the term “mpy,” refers to “milli-inch per year” and is used herein as a unit of measurement of the General Corrosion rate of metal/metal alloy surfaces in the presence of copper or a copper corroding agent such as sodium hypochlorite.

For the purposes of the present invention, the term “General Corrosion” also called “Uniform Corrosion”) refers to corrosion which takes place uniformly over the surface of metal/metal alloy surfaces in the presence of a corrosive agent, thereby causing a uniform removal of metal/metal alloy from the surface and thus a general thinning of the component comprising the metal/metal alloy. General Corrosion should be contrasted with “localized corrosion” such as pitting corrosion, crevice corrosion, etc. General Corrosion rates are measure herein as described in the Measurement of General Corrosion Rates section described below.

For the purposes of the present invention, the amounts referred to herein in terms of weight percent for the tetrahydrobenzotriazoles, other triazoles, tetrahydrobenzotriazole activating solvents, etc., refer to single strength usage amounts where the composition is in a ready to use form. Accordingly, the compositions comprising these tetrahydrobenzotriazoles, other triazoles, tetrahydrobenzotriazole activating solvents, etc., may also be in concentrate form in amounts which provide, after appropriate dilution with, for example, water, organic fluids, etc., single strength usage compositions having the requisite weight percent ranges of tetrahydrobenzotriazoles, other triazoles, tetrahydrobenzotriazole activating solvents, etc., as hereafter specified.

For the purposes of the present invention, the formulas used in the specification, in the claims or in the drawings may represent a single compound, a mixture of compounds, etc., unless otherwise specified.

Description

Copper corrosion issues may occur in various forms. For example, copper corrosion may occur in one of two general forms, one direct and one indirect. In the direct form of copper corrosion, a metal component comprising copper or copper alloy may be chemically attacked by a copper corroding agent such as chlorine, a hypochlorite, etc., which may be used, for example, as an oxidizing biocide in, for example, an industrial water system. Direct chemical attack on the surface of the metal component may cause a general thinning and weakening of the component due to loss of copper metal (i.e., General Corrosion), or may cause localized corrosion (e.g., pitting corrosion crevice corrosion, etc.) of the metal component. In addition to causing thinning and weakening of the metal component, direct copper corrosion may create an increasingly concentrated copper-containing effluent in any fluid (e.g., water) which comes into contact with the corroding metal component. Disposing of this copper-containing effluent may pose a significant environmental and toxicity problem. Also, the copper-containing effluent may itself catalytically attack organic (e.g., hydrocarbon)-containing materials present in the effluent or in other components in the system, thus causing other undesirable effects.

In the indirect form of copper corrosion, copper ions present in the fluid (e.g., from direct corrosion of metal components) may come into contact with other metal components. These other metal components may comprise metal or metals alloys such as aluminum, steel, iron, etc., which, when contacted with the fluid carrying the copper ions, may cause the copper ion to “plate out” on the surface of the metal component. Because many of such copper ion-containing fluids may also function as electrolytes, the copper that “plates out” on the metal component may then cause an electrochemical process of galvanic corrosion where the aluminum, iron, steel, etc., is electrochemically dissolved from the surface of the metal component to again cause general thinning/weakening (i.e., General Corrosion) of the metal component, as well as localized corrosion (e.g., pitting corrosion crevice corrosion, etc) thereof.

Embodiments of the corrosion inhibiting compositions and methods of the present invention are directed at controlling, and especially inhibiting, the corrosive effects of copper due to either direct or indirect corrosion of copper or copper alloys. Certain benzotriazoles such as benzotriazole (“BT”) and tolyltriazole (“TT”) are commonly used as corrosion inhibitors for protecting metal/metal alloy components, such as those comprising copper and copper alloys (e.g., brass), from direct corrosion caused by copper corroding agents. These benzotriazoles may also be used to “scavenge” copper present in the fluids circulating through these systems to minimize, reduce, decrease, etc., indirect galvanic corrosion of metal/metal alloy components (e.g., those comprising aluminum, iron, steel, etc.) caused by the copper in such fluids “plating out.” But even when such metal/metal alloy components protected by such benzotriazoles (e.g., as a protective film on the surface of the component) are exposed to, for example, oxidizing biocides such as chlorine, hypochlorite, etc., the corrosion protection of these films may break down. After such breakdown, it may be difficult to form new protective benzotriazole films in these aqueous systems that are periodically or continuously supplied with oxidizing biocides such as chlorine, hypochlorite, etc. Very high dosages of, for example, tolyltriazole (TT) may be applied in an attempt to improve corrosion inhibition performance, but may provide limited success.

What has been discovered to be surprising with respect to the embodiments of the corrosion inhibiting compositions of the present invention is that the corrosion inhibition properties of these benzotriazoles with respect to direct corrosion of copper and copper alloys (including minimizing, reducing, decreasing, etc., the effects of dissolved copper present in the effluent such as catalytically attacking organic materials, creating environmental and toxicity issues, etc.), as well as indirect galvanic corrosion caused by copper ions “plating out” on other metals and metal alloys, such as aluminum, iron, steel, etc., may be further improved by blending in certain minimal amounts of certain tetrahydrobenzotriazoles, such tetrahydrotoluyltriazole (“THTT”), even in the presence of, for example, oxidizing biocides such as chlorine, hypochlorite, etc. In fact, it has been surprisingly found that in embodiments of corrosion inhibition compositions of the present invention that the combination of, for example, tetrahydrotolyltriazole (“THTT”) with a blend of benzotriazole (“BT”) and tolyltriazole (“TT”), performs better as a corrosion inhibitor than simply using THTT alone. What has also been found to be particularly surprising is that amount of for example, THTT should be adjusted appropriately, relative to the amount of, for example, BT/TT in terms of how much THTT should be blended with BT/TT, to provide improved corrosion inhibition.

In addition, in some embodiments, it has been additionally discovered that the use of certain tetrahydrobenzotriazole activating solvents, such as propylene glycol, and polypropylene glycol, etc., may minimize, reduce, lessen, diminish, avoid, prevent, eliminate, etc., the potentially “variable” corrosion inhibiting properties of these tetrahydrobenzotriazoles, even when these tetrahydrobenzotriazoles are used in combination with these other triazoles. These benefits may be achieved by solubilizing these tetrahydrobenzotriazoles in these tetrahydrobenzotriazole activating solvents, such as propylene glycol, polypropylene glycol, etc. Solubilization of these tetrahydrobenzotriazoles in these activating solvents minimizes, reduces, lessens, diminishes, avoids, prevents, eliminates, etc., micelle formation of these tetrahydrobenzotriazole in the presence of, for example, aqueous systems, and thus keeps these tetrahydrobenzotriazoles “active” as corrosion inhibitors when use in combination with these other triazoles. See co-pending U.S. application Ser. No. 13/045,580 (to William N. Matulewicz et al.), filed Mar. 11, 2011, the entire disclosure and contents of which is herein incorporated by reference.

Embodiments of the corrosion inhibiting compositions of the present invention may comprise, for example, from about 10 to about 100%, such as from about 10 to about 90% (e.g., from about 35 to about 70%) by weight of the composition of a corrosion inhibitor component which comprises: one or more tetrahydrobenzotriazoles (having the general formulas Ia/Ib defined above, including salts of these tetrahydrobenzotriazoles); and one or more other triazoles (having the general formula II defined above, including salts of these other triazoles). The weight ratio of the tetrahydrobenzotriazoles to the other triazoles are such that the composition decreases the General Corrosion rate, as measured by copper electrodes in the presence of 10 ppm sodium hypochlorite, by at least about 0.05 mpy (for example, at least about 0.3 mpy, such as at least about 0.5 mpy) relative to a corrosion inhibitor component comprising 100% of the other triazoles. For example, the weight ratio of these tetrahydrobenzotriazoles to these other triazoles may be in the range of from about 1:89 to about 1:8, such as from about 1:89 to about 1:12 (e.g., from about 1:44 to about 1:14).

Embodiments of the corrosion inhibiting components comprising the one or more tetrahydrobenzotriazoles with the other triazoles may be prepared simply by blending together the constituent compounds or by blending together the precursors of the constituent compounds and then hydrogenating those precursors. Initial hydrogenation of, for example, the methylbenzotriazole isomers may be accomplished by catalytic hydrogenation processes known in the art. See, for example, U.S. Pat. No. 3,597,353 (Randell et al.), issued Aug. 3, 1971; and U.S. Pat. No. 3,849,433 (Butula et al.), issued Nov. 19, 1974, the entire contents and disclosures of which are herein incorporated by reference, for how to prepare tetrahydrobenzotriazoles from the respective benzotriazoles by catalytic hydrogenation, and which may also provide residual unhydrogenated benzotriazoles as the other triazoles for embodiments of compositions of the present invention. Commercially available liquid mixtures of THTT (e.g., a mixture of 4-methyl-1H-benzotriazole and 5-methyl-1H-benzotriazole) may include the trade name product “Cemazol WD-85” available from CEMCO, Inc., the trade name product “COBRATEC 928,” available from PMC Specialties Group, Inc., etc.

Embodiments of the corrosion inhibiting compositions of the present invention comprising the one or more tetrahydrobenzotriazoles, other triazoles, and optionally tetrahydrobenzotriazole activating solvents may also comprise other optional ingredients, and/or may be used with such optional ingredients. For example, these optional ingredients may include: water, organic fluids; biocides, fungicides or other bactericidal agents; extreme pressure additives; antioxidants: other corrosion inhibitors besides tetrahydrobenzotriazoles and other triazoles; dyes; water conditioners; pH-controlling agents; perfumes; viscosity-controlling agents; etc.

The embodiments of the compositions of the present invention may be used in a variety of processes, systems, etc., where metal components comprising copper or copper alloy are potentially subject to direct corrosion by being chemically attacked by copper corroding agents, such as for example, chlorine, a hypochlorite, etc., as well as indirect copper corrosion where copper ions present in the fluid may come into contact with metal components comprising metal or metals alloys such as aluminum, steel, iron, etc., on which these copper ions may “plate out” and thus cause galvanic corrosion. These processes, systems, etc., may be aqueous or nonaqueous, and may include, for example, industrial aqueous processes and systems, heat exchanger/transfer systems, metal working processes, machining fluid systems, coolant systems (e.g., cooling water systems), lubricant systems, hydraulic fluid systems, boilers and similar steam generating systems, reverse osmosis processes and systems, oil production processes and systems, flash evaporator processes and systems, desalinization processes and systems, gas scrubber systems, blast furnace systems, paper and pulp processing systems, food and beverage processing systems, bottle washing processes and systems, soil irrigation systems, aqueous-based closed circuit heating or refrigerant systems, polymer coating systems, sewage effluent systems, industrial waste water systems, etc.

In embodiments of the method of the present invention, the corrosion inhibiting composition may be used by directly contacting the metal component (e.g., by treating, applying, forming a film, coating, dipping, spraying, wiping, daubing, etc.) with the composition, or by incorporating, adding, blending, mixing, etc., the composition to a fluid which contacts the metal component. The amount of the corrosion inhibiting composition to be used to provide corrosion inhibition will depend on a variety of factors, including, for example, the particular corrosion inhibition component used and concentration in the composition, the particular process, system, etc., that the corrosion inhibiting composition is used with, the degree of potential corrosion expected in the particular process, system, etc., the manner in which the corrosion inhibiting composition is used, added, incorporated, etc., to inhibit corrosion, etc. For example, providing an amount of the corrosion inhibiting composition which creates a concentration of at least about 1 ppm (such as from about 50 to about 1000 ppm of the composition, e.g., from about 100 to about 500 ppm of the composition, such as from about 250 to about 500 ppm) of the corrosion inhibition component in the fluid circulating in the process, system, etc., may provide effective corrosion inhibition.

Aspects of the embodiments of the corrosion inhibiting compositions of the present invention are illustrated by the graphs shown in the FIGURE. The FIGURE represents a graph, indicated generally as 100, which compares the General Corrosion rates (at 25° C.), as measured by copper electrodes, reflected in units of milli-inches per year (mpy), in the presence of 10 ppm sodium hypochlorite (added as two separate 5 ppm aliquots) in the aqueous test solution in which the copper electrodes (i.e., cathode, anode and reference electrodes) are immersed. The copper electrodes are “passivated” for 60 minutes with (i.e., coated with a film of) each of eight compositions (represented as individual data points 101 through 109 positioned along line 112 in graph 100 of FIG. 1) comprising 90% by weight of various blends of tetrahydrotolyltriazole (THTT) with a 50/50 mixture of tolyltriazole (TT)/benzotriazole (BT), along with 10% by weight propylene glycol. After the copper electrodes have been “passivated” for 60 minutes with each of composition, the first 5 ppm aliquot of the sodium hypochlorite is added to each composition. The second 5 ppm aliquot of sodium chlorite is added each composition approximately 15 minutes after the first aliquot. The General Corrosion rate of each composition is then measured as an individual data point approximately 3 minutes and 50 seconds after the second aliquot of 5 ppm sodium hypochlorite is added.

The various triazole blends for compositions 101 through 109, along with the respective individual General Corrosion rate data points measured (see Measurement of General Corrosion Rates section below) are shown below in Table 1:

TABLE 1 General Corro- Com- sion posi- Rate tion TTHB¹ TT² BT³ (mpy) 101  0%   45% (1 ppm)   45% (1 ppm) 0.74 (0.00 ppm) 102  1% 44.5% (0.99 ppm) 44.5% (0.99 ppm) 0.28 (0.02 ppm) 103  2%   44% (0.98 ppm)   44% (0.98 ppm) 0.19 (0.04 ppm) 104  4%   43% (0.955 ppm)   43% (0.955 ppm) 0.09 (0.09 ppm) 105  6%   42% (0.935 ppm)   42% (0.935 ppm) 0.20 (0.13 ppm) 106  7% 41.5% (0.92 ppm) 41.5% (0.92 ppm) 0.36 (0.16 ppm) 107  9% 40.5% (0.90 ppm) 40.5% (0.90 ppm) 0.52 (0.20 ppm) 108 10%   40% (0.89 ppm)   40% (0.89 ppm) 0.66 (0.22 ppm) 109 30%   30% (0.665 ppm)   30% (0.665 ppm) 1.18 (0.67 ppm) ¹Tetrahydrotolyltriazole ²Tolyltriazole ³Benzotriazole

The General Corrosion rate data points for compositions 101 through 109 from Table 1 above are plotted in graph 100 of FIG. 1 as individual data points 101 through 109. As Table 1 and graph 100 in FIG. 1 show, replacing the 50/50 mixture of TT/BT with, for example, 1% to 10% THTT (see data points 102 through 108), or a weight ratio of TTHT to the TT/BT mixture in the range of from about 1:89 to about 1:8, decreases the General Corrosion rate, as measured by the Cu Electrodes in the presence of 10 ppm sodium hypochlorite, by at least 0.05 mpy relative to the 100% TT/BT mixture (see data point 101). As Table 1 and graph 100 in the FIGURE also show, replacing the 50/50 mixture of TT/BT with, for example, 1% to 7% THTT (see data points 102 through 106), or a weight ratio of TTHT to the TT/BT mixture in the range of from about 1:89 to about 1:12, decreases the General Corrosion rate, as measured by the Cu Electrodes, by at least 0.3 mpy relative to the 100% TT/BT mixture (see data point 101). As Table 1 and graph 100 in the FIGURE further show, replacing the 50/50 mixture of TT/BT with, for example, 2% to 6% THTT (see data points 103 through 105), or a weight ratio of TTHT to the TT/BT mixture in the range of from about 1:44 to about 1:14, decreases the General Corrosion rate, as measured by the Cu Electrodes, by at least 0.5 mpy relative to the 100% TT/BT mixture (see data point 101).

Measurement of General Corrosion Rates

The General Corrosion rates of the corrosion inhibitor compositions/solutions are measured herein as follow:

Equipment Used:

Pepper1 Fuchs Corr Tran MV Unit

Hart Modem, Model HI-321 (Pepper1 Fuchs)

99.9% Cu Electrodes (CME-OJ) (Pepper1 Fuchs)

Corr Tran MV Unit Operating Conditions Used:

HDA (Harmonic Distortion Analysis) PV Units: mpy Electrode Area: 4.75 cm² LRV: 0 mpy K Probe Constant: 11685.71 mm^(x)cm²/y/A URV: 40 mpy Measurement Mode: GC + Con Alarm: Auto Device Mode: Standard Cyclic/On PV Preference: General Solution/Reagent/Equipment Component Preparation:

-   -   1. Corrosive water solutions are prepared according to ASTM         D1384-05 Specifications     -   2. Preparation of Electrodes: Electrodes (i.e., cathode, anode         and reference electrodes) used for testing are “conditioned” by         using the electrodes a few times and then cleaning electrodes to         obtain the most consistent performance. After electrode use, the         electrodes are removed from the Corr Tran unit and are cleaned         with pumice powder and deionized water until the electrode         surface is free of any inhibitor composition or corrosive film.         The electrodes are rinsed in HCl (0.1N) for ten seconds,         followed by rinsing in deionized water to remove HCl on the         surface, and are then polished with clean paper towels. An air         hose (oil-free) may be used to remove any liquid from the         electrode surface.     -   3. Preparation of Corrosion Inhibitor Compositions/Solutions: An         appropriate quantity of corrosion inhibitor composition/solution         is added to 10.000 ml of HPLC grade methanol.         Procedure for Measuring General Corrosion Rates:

The methanol-containing corrosion inhibitor compositions/solutions are added in an amount of 1.00 ml to 1 liter of the prepared corrosive water solution and stirred. After stirring is started, the Cu electrodes (i.e., cathode, anode and reference electrodes) are immersed two inches below the top surface of the corrosive water solution. Corrosion data is then recorded on Corr Tran MV Unit, using the Operating Conditions described above. After immersion (“passivation”) in the corrosive water solution for 60 minutes, the first 5 ppm aliquot of sodium hypochlorite (prepared from 6.15% active sodium hypochlorite bleach) to the corrosive water solution. Approximately 15 minutes after the first aliquot is added, a second 5 ppm aliquot of sodium hypochlorite (also prepared from 6.15% active sodium hypochlorite bleach) is added to the corrosive water solution. General Corrosion rate data points are recorded for up to 120 minutes (2 hours) after initial immersion of the Cu Electrodes in the corrosive water solution. The General Corrosion rate data recorded may be used as an individual General Corrosion rate data points (measured approximately 3 minutes and 50 seconds after the second aliquot of 5 ppm sodium hypochlorite is added as shown by individual data points 101 through 109 of graph 100 in the FIGURE), or may be graphically plotted continuously.

All documents, patents, journal articles and other materials cited in the present application are hereby incorporated by reference.

Although the present invention has been fully described in conjunction with several embodiments thereof, it is to be understood that various changes and modifications may be apparent to those skilled in the art. Such changes and modifications are to be understood as included within the scope of the present invention as defined by the appended claims, unless they depart therefrom. 

What is claimed is:
 1. A method comprising the following steps: (a) providing a composition comprising a corrosion inhibiting component having: one or more tetrahydrobenzotriazoles having the general formulas Ia or Ib:

wherein R₁ is one or more of: hydrogen, a hydroxy group, or an aliphatic group, and wherein R₂ is hydrogen, or an aliphatic group, or a salt of the tetrahydrotriazoles; and one or more other triazoles having the general formula II:

wherein R₃ is one or more of: hydrogen, a hydroxy group, an aliphatic group, or an aromatic group, R₄ is hydrogen, or an aliphatic group; or a salt of the other triazoles; wherein the tetrahydrobenzotriazoles are in a weight ratio to the other triazoles in the range of from about 1:89 to about 1:8 such that the composition decreases the General Corrosion rate, as measured by copper electrodes in the presence of 10 ppm sodium hypochlorite, by at least about 0.05 mpy relative to a corrosion inhibitor component comprising 100% of the other triazoles; wherein the corrosion inhibiting component comprises from about 10 to 100% of the composition; and (b) contacting a metal component which is corrodible in the presence of copper or copper corroding agents with the composition of step (a) to inhibit corrosion of the metal component by copper or copper corroding agents; wherein step (b) is carried out by incorporating the composition of step (a) in a fluid which is in contact with the metal component such there is a concentration of the corrosion inhibiting component in the fluid of at least about 1 ppm.
 2. The method of claim 1, wherein the metals or metal alloy of step (b) comprises copper.
 3. The method of claim 2, wherein step (b) is carried out by forming a protective film of the composition of step (a) on a surface of the metal component.
 4. The method of claim 1, wherein the metal or metal alloy of step (b) is one or more of: aluminum, iron, steel, or silver.
 5. The method of claim 4, wherein the metal component is in the presence of a copper-containing fluid and wherein step (b) is carried out by adding the composition of step (a) to the copper-containing fluid.
 6. The method of claim 1, wherein the metal component of step (b) is part of an aqueous system.
 7. The method of claim 1, wherein the metal component of step (b) is part of a nonaqueous system.
 8. The method of claim 1, wherein the metal component of step (b) is part of a heat exchanger/transfer system, a machining fluid system, a coolant system, a lubricant system, a hydraulic fluid system, a steam generating system, a reverse osmosis system, an oil production system, a flash evaporator system, a desalinization system, a paper processing system, a pulp processing system, a food processing system, a beverage processing system, a bottle washing system, an aqueous-based closed circuit heating system, an aqueous-based closed circuit refrigerant system, a sewage effluent system, or an industrial waste water system.
 9. The method of claim 1, wherein step (b) is carried out by incorporating the composition of step (a) in the fluid such that there is a concentration of the corrosion inhibiting component in the fluid of from about 50 to about 1000 ppm.
 10. The method of claim 1, wherein the one or more tetrahydrobenzotriazoles of the composition of step (a) are one or more of: tetrahydrobenzotriazole; or tetrahydrotolyltriazole.
 11. The method of claim 10, wherein the one or more tetrahydrobenzotriazoles of the composition of step (a) are tetrahydrotolyltriazole.
 12. The method of claim 1, wherein the one or more other triazoles of the composition of step (a) are one or more of: benzotriazole; a sodium salt of benzotriazole; tolyltriazole; a sodium salt of tolyltriazole; pentoxy-benzotriazole; carboxy-benzotriazole; N-1-bis(2-ethylhexyl)-aminomethyl-tolyltriazole; or N-1-bis(2,2′-ethanol)-aminomethyl-tolyltriazole.
 13. The method of claim 12, wherein the one or more other triazoles of the composition of step (a) are a mixture of benzotriazole and tolyltriazole, or a mixture of the sodium salts of benzotriazole and tolyltriazole.
 14. The method of claim 1, wherein the weight ratio of the tetrahydrobenzotriazoles to the other triazoles of the composition of step (a) is in the range of from about 1:89 to about 1:12.
 15. The method of claim 14, wherein the weight ratio of the tetrahydrobenzotriazoles to the other triazoles of the composition of step (a) is in the range of from about 1:44 to about 1:14.
 16. The method of claim 1, wherein the weight ratio of the tetrahydrobenzotriazoles to the other triazoles is such that the composition of step (a) decreases the General Corrosion rate, as measured by the copper electrodes in the presence of 10 ppm sodium hypochlorite, by at least about 0.3 mpy relative to the corrosion inhibitor component comprising 100% of the other triazoles.
 17. The method of claim 16, wherein the weight ratio of the tetrahydrobenzotriazoles to the other triazoles is such that the composition of step (a) decreases the General Corrosion rate, as measured by copper electrodes in the presence of 10 ppm sodium hypochlorite, by at least about 0.5 mpy relative to the corrosion inhibitor component comprising 100% of the other triazoles. 